Compositions and methods for improved encapsulation of functional proteins in polymeric vesicles

ABSTRACT

Methods of preparing polymersome-encapsulated functional protein suspensions may include thermally blending an amount of a block copolymer with an amount of a low molecular weight polyethylene glycol (PEG) for at least 30 minutes, mixing and cooling a resulting PEG/polymer formulation to room temperature, adding an aliquot of a solution of the functional protein to a sample containing the PEG/polymer formulation, and performing at least three dilution steps in which polymersomes that are generated are progressively saturated with the functional protein. The aliquot of the solution of the functional protein added may have a to the PEG/polymer sample of around 0.5:1 to 1.5:1 by volume, and the thermal blending may be performed at 90-100° C.

RELATED APPLICATIONS

This application claims the benefit of priority to U.S. ProvisionalPatent Application Ser. No. 62/187,942, filed on Jul. 2, 2015, theentire content of which is hereby incorporated by reference.

STATEMENT AS TO FEDERALLY SPONSORED RESEARCH

Work on this invention was supported by funds from the NationalInstitute of Health (Study ID#1R43CA159527-01A1 and StudyID#1R43AI096605-01). The United States Government therefore has certainrights in this invention.

BACKGROUND

Natural and synthetic proteins offer an incomparable array of uniquebiological functions that may be exploited for human therapeuticapplications. Their clinical utility, however, is often limited bybiochemical instability, poor pharmacologic properties, and potential toinduce adverse immunogenicity. Incorporation of biomolecules, such asproteins, in long-circulating vehicles with attached polyethylene glycol(PEG) polymer chains (i.e., PEGylated vehicles), such as nanoparticles,may mitigate such issues. However, the stable encapsulation of largequantities of functional proteins in PEGylated vehicles has proven to bechallenging. Conventional encapsulation techniques, which wereoriginally developed for small-molecule drug delivery, require the inputof high energies and/or the use of organic solvents for particleformation, and are therefore unsuitable for use with biologicallycomplex and more labile macromolecules.

In particular, examples of conventional encapsulation techniques mayinclude thin-film rehydration, direct-hydration, and electro-formation,which may be used to encapsulate small molecules and proteins withunique biological function into polymersomes generated frompoly(ethylene oxide)-block-poly(butadiene) (PEO-b-PBD). For example,methylene blue (mBlue; Mw=319.85 g/mol) may be used as a model smallmolecule, and myoglobin (Mb; Mw=17,600 Da) may be used a model proteinwith unique biological function (i.e., oxygen storage). The efficienciesof encapsulating methylene blue and myoglobin into PEO-b-PBD using thethin-film rehydration and direct hydration techniques have beencompared. In particular, quantification of the maximum encapsulation offully functional myoglobin was based on a number of characteristics,using these established techniques. For example, the concentration andthe reduction-oxidation reaction (“redox”) state of iron in the hemegroup of myoglobin were respectively measured using inductively coupledplasma optical emission spectroscopy (ICP-OES) and UV-Vis absorptionspectroscopy (also referred to as spectrophotometry). The morphologiesand stabilities of polymersome-encapsulated myoglobin (PEM) wererespectively verified by cryogenic transmission electron microscopy(cryo-TEM) and by dynamic light scattering (DLS). Equilibrium oxygenbinding and release at various partial pressures of oxygen were measuredusing a Hemeox analyzer. While the thin-film rehydration and directhydration techniques allowed for successful methylene blueencapsulation, encapsulation of myoglobin was uniformly poor. Therefore,improved methods for generating PEM will be beneficial for humantherapeutic applications.

SUMMARY

Various embodiments include methods of preparingpolymersome-encapsulated functional protein suspensions by thermallyblending an amount of a block copolymer with an amount of a lowmolecular weight polyethylene glycol (PEG) for at least 30 minutes,mixing and cooling a resulting PEG/polymer formulation to roomtemperature, adding an aliquot of a solution of the functional proteinto a sample containing the PEG/polymer formulation, and performing atleast three dilution steps in which polymersomes that are generated areprogressively saturated with the functional protein. In someembodiments, a ratio of the added aliquot to the PEG/polymer sample isaround 0.5:1 to 1.5:1 by volume. In some embodiments, the thermalblending is performed at 90-100° C. In some embodiments, each dilutionstep includes adding to the sample an additional amount of the solutionof the functional protein, mixing a resulting dispersion of thefunctional protein in the PEG/polymer formulation, and sonicating theresulting dispersion for at least 30 minutes.

In some embodiments, performing the at least three dilution stepsincludes performing a first, a second, and a third dilution step in aserial fashion. In some embodiments, adding the additional amount of thesolution in the first step includes adding a first amount of thesolution of the functional protein such that a ratio of the first amountto the PEG/polymer formulation is around 1:1 by volume. In someembodiments, adding the additional amount of the solution in the secondstep includes adding a second amount of the solution of the functionalprotein such that a ratio of the second amount to the PEG/polymerformulation is around 2:1 by volume. In some embodiments, adding theadditional amount of the solution in the third step includes adding athird amount of the solution of the functional protein such that a ratioof the third amount to the PEG/polymer formulation is around 5:1 byvolume. Embodiment methods may also include performing a fourth dilutionstep in which adding the additional amount of the solution in the fourthstep includes adding a fourth amount of the solution of the functionalprotein such that a ratio of the fourth amount to the PEG/polymerformulation is around 5:1 by volume. Embodiment methods may further alsoinclude removing surface-associated protein from polymersomes in thesuspension of the polymersome-encapsulated functional protein usingproteolysis after the at least three dilution steps. In someembodiments, using proteolysis includes treating the mixedPEG/polymer/protein sample with a 0.4 wt % pronase solution for at least18 hours at room temperature, and allowing dialysis of thePEG/polymer/protein sample at 4° C. for at least twelve hours.

In some embodiments, the solution of the functional protein may be a 150mg/mL solution of oxymyoglobin (oxyMb) in phosphate buffered saline(PBS). Embodiment methods may also include preparing the solution of thefunctional protein by combining a solution of 150 mg/mL metmyoglobin(metMb) in phosphate buffered saline with sufficient amount of 1 wt %sodium dithionite (Na₂S₂O₄) to reduce to the metMb to oxyMb. In someembodiments, the block copolymer may be an amphiphilic diblockcopolymer. In some embodiments, the amphiphilic diblock copolymer may bepoly(ethylene oxide)-block-poly(butadiene) (PEO-b-PBD). In someembodiments, thermally blending an amount of the amphiphilic diblockcopolymer with an amount of the low molecular weight PEG for at least 30minutes includes thermally blending 5-15 mg of poly(ethyleneoxide)-block-poly(butadiene) (PEO-b-PBD) with 5-15 mg of 500 kDa PEG(PEG500) for at least one hour. In some embodiments, thermally blendingan amount of the amphiphilic diblock copolymer with an amount of the lowmolecular weight PEG for at least 50 minutes includes thermally blending10 mg of poly(ethylene oxide)-block-poly(butadiene) (PEO-b-PBD) with 10mg of 500 kDa PEG (PEG500) for one hour. In some embodiments, thermallyblending the amount of the amphiphilic diblock copolymer with the amountof the low molecular weight PEG for at least 30 minutes may includethermally blending 10 mg of poly(ethylene oxide)-block-poly(butadiene)(PEO-b-PBD) with 10 mg of 500 kDa PEG (PEG500) for one hour. In someembodiments, adding the aliquot of the solution of the functionalprotein may include adding 10 μL of a solution of oxyMb to the samplecontaining the PEG/polymer formulation. In some embodiments, the thermalblending may be performed at around 95° C.

BRIEF DESCRIPTION OF THE DRAWINGS

The accompanying drawings, which are incorporated herein and constitutepart of this specification, illustrate exemplary embodiments, andtogether with the descriptions of various embodiments, serve to explainthe features herein.

FIG. 1 is a table of results from encapsulating a variety of proteinsusing existing techniques.

FIG. 2 is a table of properties for two poly(ethyleneoxide)-block-poly(butadiene) (i.e., PEO-b-PBD) diblock copolymers andtheir polymersome formulations used for small molecule and proteinencapsulation.

FIGS. 3A and 3B are graphs showing results from optimization of varioussteps in the direct hydration protocol to improve encapsulation ofmyoglobin in polymersomes of a particular PEO-b-PBD formulation.

FIGS. 3C and 3D are graphs showing the rate of myoglobin oxidation andthe loss of surface-associated myoglobin from proteolysis as functionsof time.

FIG. 3E is a graph showing final weight percentage compared toencapsulation efficiency of myoglobin using various ratios of myoglobinto phosphate buffered saline solution.

FIG. 4 is a table showing encapsulation results from using theprogressive saturation protocol and OB29 polymersomes to encapsulate arange of proteins according to the various embodiments.

FIG. 5A is a schematic representation of components of polymersomesprepared according to the various embodiments.

FIG. 5B is schematic representation of the existing thin-filmrehydration protocol for forming polymersome-encapsulated myoglobin.

FIG. 5C is a schematic representation of the existing direct hydrationprotocol for forming polymersome-encapsulated myoglobin.

FIGS. 6A and 6B are graphs showing results from encapsulation ofmethylene blue into polymersomes formed from a particular PEO-b-PBDformulation using existing protocols.

FIGS. 6C and 6D are graphs showing results from encapsulation ofmyoglobin into polymersomes formed from a particular PEO-b-PBDformulation using existing protocols.

FIG. 7A is a schematic representation of the progressive saturationprotocol for forming polymersome-encapsulated myoglobin in variousembodiments.

FIGS. 7B and 7C are graphs illustrating results from encapsulation ofmyoglobin into polymersomes formed from a particular PEO-b-PBDformulation using the progressive saturation protocol of FIG. 7A.

FIG. 7D is a table summarizing the results shown in FIGS. 7B and 7C.

FIG. 7E is a table showing the partial pressure of oxygen required toachieve 50% saturation (P₅₀) obtained from O₂ equilibrium curves for offree myoglobin and for polymersome-encapsulated myoglobin, prior toproteolysis and after pronase treatment, that was prepared byprogressive saturation.

FIG. 8A is a graph showing results from encapsulation of myoglobin intopolymersomes formed from two particular PEO-b-PBD formulations using theprogressive saturation technique of the various embodiments.

FIGS. 8B and 8C are cryo-TEM images of vesicles inpolymersome-encapsulated myoglobin suspensions formed from each of theparticular PEO-b-PBD formulations using the progressive saturationtechnique of the various embodiments.

FIG. 8D is a graph showing the average hydrodynamic diameters of apolymersome-encapsulated myoglobin suspension formed from a particularPEO-b-PBD formulation using the progressive saturation technique of thevarious embodiments.

FIG. 8E is a graph showing the oxygen equilibrium curves for freeoxymyoglobin and oxygenated polymersome-encapsulated myoglobinsuspension formed from a particular PEO-b-PBD formulation using theprogressive saturation technique of the various embodiments.

DETAILED DESCRIPTION

The various embodiments will be described in detail with reference tothe accompanying drawings. Wherever possible, the same reference numberswill be used throughout the drawings to refer to the same or like parts.References made to particular examples and implementations are forillustrative purposes, and are not intended to limit the scope of theclaims.

The various embodiments include improved methods for generating PEM,which may include identifying the key parameters of the thin-filmrehydration and direct hydration protocols that prevent efficient uptakeand/or compromise protein function, and performing iterativeoptimization of such key parameters. As a result, the variousembodiments provide a generalizable technique that enables theencapsulation of increased quantities of functional proteins withinneutrally charged and fully PEGylated polymer vesicles. That is, thevarious embodiments include a new “progressive saturation” method forencapsulating myoglobin in polymersomes.

Nanoparticle vehicles may overcome many challenges associated with thedelivery of functional proteins to enable the clinical development ofdiverse macromolecular pharmaceuticals. Nanoparticle vehicles mayinclude, for example, liposomes (i.e., self-assembled vesicles ofnatural phospholipids) and polymersomes (i.e., self-assembled polymervesicles of block copolymers), as well as micelles, perfluorocarbonemulsions, and others. To that end, polymersomes, have advantageousproperties as compared to conventional liposomes, as liposomes typicallyhave high membrane permeability and low stability in vivo. There havebeen, however, few comparative studies to establish and validated asingle, scalable and generalized strategy for encapsulating largeamounts of protein in neutrally charged and/or PEGylated polymersomes.By optimizing and combining different steps from various liposome-basedencapsulation methods, the various embodiments provide a new progressivesaturation technique that allows improved encapsulation of functionalproteins in nanoscale polymer vesicles. The various embodimentsdemonstrate a tradeoff between the degree of polymersome loading (i.e.,weight percentage of protein-to-polymer) and the encapsulationefficiency of protein (with respect to the initial quantity that wasemployed for polymersome formation) that may be achieved. Moreover, inthe various embodiments, a proteolysis step accurately quantifies theamounts of both encapsulated protein (i.e., the desired outcome) as wellas surface associated (i.e., non-specifically bound) product that may beobtained in polymersome suspensions formed by the progressive saturationprotocol. While there are some reports of large amounts of proteinloading within polymersomes at high efficiencies using existing liposomeencapsulation techniques, such reports do not involve differentiatingbetween encapsulated and surface-associated protein. Therefore, theprogressive saturation technique in the various embodiments may providea more robust, scalable, and generalizable strategy for encapsulation ofproteins in fully PEGylated and neutrally charged polymersomes inquantities and at efficiencies that may enable further translationaldevelopment.

Selective and potent modulation of protein function in mammalian cellsis the principal activity of most molecular therapeutics, where the vastmajority of available agents are organic small molecules (less than orequal to 800 Da in size). Recent studies suggest, however, that only asmall percentage of the human proteome is susceptible to smallmolecule-based therapy. Moreover, the functional diversity of proteinsthat are successfully targeted by small molecules remains very low. Thatis, around 40% of all prescription drugs target a single class ofproteins, namely the G-protein coupled receptors. However, use ofsmall-molecule therapy is limited since small drug molecules areintrinsically unable to cope with the extended contact surfaces found atmany biologically important interfaces.

Biomacromolecules such as proteins have recently shown significantclinical utility, in large part due to their ability to overcome thesesignificant limitations associated with traditional small moleculetherapies. When compared to the interaction of a small-molecule with itsbiological target, macromolecular therapeutics have higher foldingenergies (typically around 7-20 kcal/mol) that allow for the adoption oflarger and more precise three-dimensional configurations, which areoften required for efficient binding and/or control of complexbiological function. As such, macromolecules may achieve superiorbinding selectivity and more potent on-target activity. Currently, asmall number of macromolecular therapies in use, including theapproximately 200 protein drugs available worldwide, have demonstrated ahigh potential as new leads in drug development. Nevertheless, severalbarriers have hindered the ready development of macromolecules as humantherapeutics, including: (i) the difficulty and/or expense of commercialscale production, (ii) biochemical instability that occurs inpathophysiologic environments or with prolonged storage, (iii) shortcirculatory half-lives and large steric hindrance that prevent effectivetissue penetration, and (iv) risks associated with their potential topromote severe adverse effects, such as the induction of anti-idiotypicantibodies and/or immune complex formation. To overcome some of theselimitations, most pharmaceutical compounds either employ biocompatiblepolymers (e.g., polyethylene glycol (PEG) or hyaluronic acid) orliposomes (i.e., lipid based vesicles) for protein complexation and invivo delivery.

Synthetic nanoparticles may exhibit superior properties to enhance drugdelivery when compared to more conventional formulations. In particular,among the classes of nanoparticles, polymersomes (i.e., self-assembledpolymer vesicles comprised of amphiphilic block copolymers) may providea beneficial nanoscale delivery platform. While lipid-based vesicles(i.e., liposomes) have been extensively utilized in biomedical research,there are material limitations inherent to these phospholipid-based drugdelivery vehicles, including compromised suspension stability, prematuredrug release, and limited product shelf-life. In contrast, polymersomesare formed from higher molecular weight amphiphilic block copolymersthat impart a broad and tunable range of carrier properties. Forexample, polymersomes enable: (i) facile and stable loading of diversetherapeutic payloads through non-covalent interactions, (ii) mechanicalstability that is 5 to 50 times greater than that of liposomes ormicellar structures constructed from similar molecular weightcopolymers, (iii) economic and large scale production that removes theneed for costly post-manufacturing purification, and (iv) diversity inbiochemical properties, which are imparted by their construction from avariety of copolymer compositions. Such properties may include fullyPEGylated surfaces and tunable in vivo circulation times, site-specifictargeting, environmental responsiveness, and complete biodegradation.

The incorporation of proteins into nanoparticles may enhance theirpharmacologic performance and improve their on-target activity. Methodsthat have been developed for encapsulating proteins into nanoparticleshave utilized electrostatic interactions to incorporate a handful ofhighly anionic proteins, or chemical or genetic modification of theoriginal protein for efficient and reproducible nanoparticle formation.Examples of such method include thin-film rehydration (i.e., rehydrationof dried polymer), which results in low yields ofpolymersome-encapsulated protein. Another example method is directhydration, the use of which is generally limited to small-scalepreparations (e.g., less than one mL). Another example method iselectro-formation, which provides useful results for only a limitednumber of proteins (i.e., highly charged proteins). Another examplemethod is hollow-fiber extrusion, which involves extrusion of preformedvesicles in the presence of protein solution. While the hollow-fiberextrusion technique has been used for large-scale preparations ofliposome-encapsulated protein, elevated temperatures and pressures arerequired for polymersome formation, which has limited its widespreadapplicability.

Existing techniques require the input of thermal, electric, ultrasonic,or mechanical energy for particle formation, or alternatively the use oforganic cosolvents, which may damage the structure and/or function ofthe protein, making encapsulation more challenging and limited inutility. Therefore, in various encapsulation techniques, a need existsfor a generalized method that enables the incorporation of largequantities of native protein in neutrally charged and/or PEGylatednanoparticles.

While adoption of various liposome encapsulation techniques has enabledfacile incorporation of small molecules within polymersomes, thesemethods cannot directly be applied for scalable encapsulation of thefunctional proteins. Often, there is a trade-off in the maximumconcentration of the aqueous protein that may be encapsulated (i.e., mgprotein/mL solution), the final loading ratio of protein-to-polymer thatcomprises the polymersome structure (i.e., w/w % protein/polymer),and/or the protein encapsulation efficiency (i.e., the percentage of theinitial protein suspension that is retained). Further, the value of eachof these parameters is highly dependent on the nature of the protein,the exact block copolymer formulation, and the encapsulation method thatis utilized. For example, the table in FIG. 1 shows existing resultsfrom encapsulation of various proteins into polymersomes. The variousembodiments provide an alternative, optimized and reproducible method toefficiently encapsulate increased quantities of functional proteins inpolymersomes. The newly developed “progressive saturation” technique ofthe various embodiments is readily scalable, highly reproducible, andgeneralizable for producing increased quantities ofpolymersome-encapsulated protein that may enable new and diversebiomedical applications.

In various embodiments, PEO-b-PBD copolymers are used to formpolymersomes that possess fully PEGylated surfaces. Such surfaces, beinguncharged and nondegradable; provide an ideal system for ensuringvesicle integrity and minimizing unwanted protein interactions ormodifications. Two different molecular weight PEO-b-PBD polymers, “OB18”diblock copolymer and “OB29” diblock copolymer, are employed todetermine the generalizability of the results as they pertain topolymersomes of different minimal sizes, PEG lengths, and membrane corethicknesses. FIG. 2 provides a table showing a comparison of variousproperties of OB18 and OB29. Methylene blue (mBlue; Mw=319.85 g/mol),which is highly stable in aqueous suspension and has a strongnear-infrared absorbance enabling ready spectrophotometric detection, isused as a model small molecule to establish various baseline parametersfor encapsulation using existing methods. Such baseline parametersinclude aqueous suspension concentration, final weight percentage, andencapsulation efficiency. Myoglobin (Mb; Mw=17,600 Da), which has a sizeand thermal stability (i.e., denaturation above 60° C.) comparable toother small proteins with therapeutic potential, was used as a modelprotein. Myoglobin also has a strong ultraviolet (UV) absorbance thatenables ready identification of its functional status, as determined bythe redox state of its iron-containing heme group. Myoglobin hasadditionally been employed in other studies, enabling comparisons ofresults to other encapsulations using existing techniques, as discussedabove with respect to FIG. 1. Methylene blue is easily encapsulated inPEO-b-PBD polymersomes formed by thin-film rehydration at elevatedtemperatures, yielding final weight ratios of mBlue-to-polymer of 4.1and 5.0 w/w % when formed at 40 and 60° C., respectively. However,similar conditions only led to myoglobin degradation.

When vesicles are formed by thin-film rehydration, as the film of drycopolymer is hydrated, lamellae (aka sponge-like structures) are firstformed as the hydrophilic blocks in the film swell. Further swellingleads to transformation into hexagonally packed vesicles and finallyinto fully dispersed polymersomes. When thin-film rehydration isattempted in solutions of soluble small molecules (or proteins), thesewater-soluble species adsorb to the surfaces of the budding lamellae,which subsequently adopt a spontaneous (or preferred) curvature. Duringformation, these membranes preferentially bend away from the aqueouscompartment that contains the higher concentration of adsorbing species,thereby excluding the water-soluble agents from vesicle encapsulation.Ultimately, the input of energy can overcome this spontaneous surfacetension in order to promote vesicle encapsulation. The amount of energythat is required scales with the size of the adsorbed molecule and themembrane thickness of the vesicle. Thus, while it is easy to disruptliposomes and enable effective small molecule and protein loading bythin-film rehydration by the input of thermal (and/or sonic) energy,such input is only enables effective encapsulation of small moleculesinto polymersome suspensions. In the direct hydration method, which wasdeveloped as a hybrid of solvent dispersion and homopolymer addition,the hydrophilic polymer PEG500 dimethyl ether (DME) is used to disruptthe interactions of hydrophobic chains in the forming polymer lamellae.With subsequent additions of aqueous solution, self-assembly of vesiclesfrom budding lamellae that have dispersed protein is promoted andresults in improvements in aqueous encapsulation; encapsulationefficiencies as high as 37% have been observed. Using direct hydrationat 23° C., polymersome-encapsulated myoglobin suspensions may haveencapsulation efficiencies greater than 10%, with the encapsulatedmyoglobin species exhibiting good suspension properties and thecharacteristic absorption spectra of intact protein. The final loadingof myoglobin in these polymersome-encapsulated suspensions, however, wasfound to be only around 0.3 w/w % Mb/polymer. Upon addition of aprotease solution to induce proteolysis of all surface associated (i.e.,non-specifically bound) protein, the final Mb composition of PEMsuspensions was found to be even lower—that is, less than 0.1 w/w %Mb/polymer. For translational therapeutic applications, the loading oftherapeutic proteins within the aqueous cavities of polymersome vehiclesis ultimately the metric that must be maximized in order to minimize theamount of associated carrier that is introduced to a subject. Therefore,such encapsulation using standard direct hydration is insufficient.

In various embodiments a progressive saturation protocol provides forefficient generation of PEM suspensions. The generalizability ofprogressive saturation for protein encapsulation is further establishedby utilizing a variety of different proteins, ranging from 17-450 kDa,yielding nanoscale polymersomes in quantities that may enablepreclinical investigations of many novel therapeutic compositions. Inparticular, a difference between the progressive saturation method anddirect hydration may involve adding five subsequent volumes of thefunctional protein solution to dilute the PEG/polymer mixture in lieu ofadditional dilutions with phosphate buffered saline (PBS).

Specifically, the progressive saturation method of the variousembodiments involves heating 10 mg of polymer and 10 mg of PEG at around95° C. for around 1 h. The sample mixture may be centrifuged and cooledto room temperature. A metmyoglobin (metMb) solution (e.g., 150 mg/mL inPBS) may be reduced to oxymyoglobin (oxyMb) with sodium dithionite(Na₂S₂O₄) (e.g., 1 wt %). From the resulting oxyMb solution, a portion(i.e., aliquot) may be added to the sample mixture at a ratio of 1:1 byvolume, and mixed thoroughly followed by sonication at room temperaturefor around 30 min. In particular, the aliquot may be 10 μL of the oxyMbsolution. The sample mixture may be further diluted with a number ofdilution steps. Specifically, each dilution step may involve addition ofa volume of the oxyMb solution (e.g., 150 mg/mL in PBS), followed bythorough mixing and sonication at room temperature for around 30minutes. The volumes of oxyMb solution used in the dilution steps may beamounts in which ratios of the oxyMb solution to the original samplemixture are 1:1, 2:1, 5:1, and 5:1 by volume 10 μL, followed by 20, 50and 100 μL. After the dilution steps, the resulting sample may besonicated for an additional 30 min at room temperature, followed bydialysis for at least 30 h at around 4° C., employing a 1000 kDamolecular weight cutoff membrane. Surface associated myoglobin may beremoved by proteolysis via treatment with 0.4 wt % pronase solution,followed by dialysis for at least 12 h at around 4° C. (e.g., molecularweight cutoff of 1000 kDa). In various embodiments, myoglobinencapsulation of the resulting polymersome suspension may be measuredbefore and after proteolysis. Specifically, concentration of myoglobinmay be measured using inductively coupled plasma optical emissionspectroscopy (ICP-OES), while redox states of iron in the heme group ofmyoglobin may be quantified using UV-Vis absorption spectroscopy.

These progressive saturation steps provided favorable results forencapsulating myoglobin in OB18 polymersomes, as shown in FIGS. 3A-3E.For example, FIG. 3A shows the final weight percentage of Mb-to-polymer(i.e., w/w % Mb/polymer) in polymersome-encapsulated myoglobin obtainedwhen no sonication was used (as in conventional techniques) and by usingsonication, according to the progressive saturation protocol (i.e., foraround 30 min at room temperature after each dilution step). A shown inFIG. 3A, a final weight percentage of Mb-to-polymer of around 6 (i.e.,w/w % Mb/polymer) may be an achieved result frompolymersome-encapsulated myoglobin created by a protocol that includessuch sonication. Therefore, sonicating the sample for around 30 min atroom temperature after each dilution step may increase encapsulationefficiency by more than 30 times based on the final weight percentageresulting from polymersome-encapsulated myoglobin generated via directhydration.

FIG. 3B shows the final weight percentage of Mb-to-polymer (i.e., w/w %Mb/polymer) in polymersome-encapsulated myoglobin obtained using ametmyoglobin solution (as in conventional techniques) and by using oxyMbas in the progressive saturation technique. FIG. 3C shows the rate ofmyoglobin oxidation (expressed as a percentage of metMb formed overtime) as a function of myoglobin exposure to different solutionconditions. FIG. 3D shows the amount of surface-associated Mb removed (%Mb loss) as a function of proteolysis time for various oxyMb volumes.FIG. 3E shows the final weight percentage of Mb-to-polymer (i.e., w/w %Mb/polymer) compared to encapsulation efficiency (% Mb EE) inpolymersome-encapsulated myoglobin generated using various ratios forthe volumes of oxyMb solution to PBS used in the dilution steps. Inparticular, the samples in FIG. 3E were proteolyzed for 18 h to removesurface-associated myoglobin, and quantified using UV-Vis absorptionspectroscopy.

Therefore, the final Mb-to-polymer weight ratios that were obtained ingenerating polymersome-encapsulated myoglobin using progressivesaturation according to various embodiments (i.e., 4-6 w/w % Mb/polymer)may be significantly improved compared to polymersome-encapsulatedmyoglobin generated using the direct hydration protocol (i.e., 0.1-0.3w/w % Mb/polymer). Without wishing to be bound to a particular theory,the loading capacity achieved using progressive saturation steps may bedue to incomplete polymersome formation during the initial dilutionstep, and further encapsulation being accomplished with each subsequentaddition of protein solution.

Developing the progressive saturation protocol included optimizing andcombining various steps from multiple liposome formation methods.Factors influencing the final concentrations of myoglobin, the relativeloading levels that could be achieved within the OB18 polymersomecarrier (i.e., w/w % protein/polymer), and the efficiency of myoglobinencapsulation were systematically evaluated. Factors such as themolecular weight of the polymer, the oxidation state and concentrationof the protein, the pH and nature of the buffered solution, the exactpolymer hydration conditions (i.e., time, temperature, and blendingtechnique), the number and duration of sonication steps, and theaddition or avoidance of freeze-thaw cycles all had effects on theconcentration and the fidelity of the final polymersome-encapsulatedprotein product.

Further, compared to polymersome-encapsulated myoglobin created usingexisting techniques, polymersome-encapsulated myoglobin created byprogressive saturation also exhibits an increase in the finalconcentrations of Mb. For example, the final concentration of Mb inpolymersome-encapsulated myoglobin generated via direct hydration isless than around 0.5 mg/ML in solution, while that ofpolymersome-encapsulated myoglobin generated via progressive saturationin the various embodiments may be greater than around 2.0 mg/mL insolution.

Using cryo-TEM to verify vesicle morphologies, suspensions ofpolymersome-encapsulated myoglobin developed using progressivesaturation showed no signs of aggregate formation when maintained at 4°C., 23° C., and 37° C. for longer than one month. The progressivesaturation technique may be further utilized for the successfulencapsulation of a variety of other proteins ranging in size from 17 to450 kDa, within PEO-b-PBD polymersomes.

Without wishing to be bound to a particular theory, there may be adirect tradeoff between Mb encapsulation efficiency and the final weightratios of Mb-to-polymer that could be achieved based on theconcentration of free Mb that was used for each addition step. Aqueousencapsulation of protein is preferred to surface-associated protein inorder to assure that the final product meets the objectives forutilizing a polymersome delivery vehicle—that is, to improve biochemicalstability, to increase circulatory half-life, to minimize adverse sideeffects, and to achieve controlled release of the associated protein.The various embodiment techniques may be employed using differentproteins that vary over a large range of molecular weights and sizes,including those associated with therapeutically relevant antibodies andenzymes. For example, the progressive saturation technique may beutilized to encapsulate myoglobin in a PEO-b-PBD-based polymersomesystem comprised of the OB29 diblock copolymer. In various embodiments,the progressive saturation technique may be utilized to encapsulate anyof a number of other proteins, including, but not limited to, antibodies(e.g., immunoglobulin G (IgG) and functional enzymes (e.g., catalase).

As described above with respect to FIG. 2, when compared to the OB18diblock copolymer, the OB29 diblock copolymer has a smaller molecularweight and generates polymersomes with a shorter PEG brush border (1.3vs. 3.9 kDa), thinner bilayer membrane (9.6 nm vs. 14.8 nm), and smalleraverage hydrodynamic diameter (130 vs. 200 nm). In various embodiments,using progressive saturation to encapsulate myoglobin in OB29polymersomes provides similar results to those from OB18 polymersomes.In various embodiments, progressive saturation technique may be appliedusing any PEG-based polymersome-forming block copolymer, including anyamphiphilic polymer comprised of PEG and a hydrophobic block that is abiodegradable polymer (e.g., a biodegradable polyester, poly(amide),poly(peptide), poly(nucleic acid), etc.). Examples of biodegradablepolyesters that may form the hydrophobic block include, but are notlimited to, poly(lactic acid), poly(glycolic acid),poly(lactic-co-glycolic acid), poly(caprolactone), poly(methylcaprolactone), poly(hydroxybutyrate), poly(hydroxyvalerate),poly(hdyroxyhexanoate), poly(hydroxyoxtanoate), and poly(trimethylenecarbonate).

The generalizability of the progressive saturation technique is furtherdemonstrated by analogous results from encapsulation of several largerproteins using OB29 polymersomes. FIG. 4 shows encapsulation resultsfrom using the progressive saturation protocol and OB29 polymersomes toencapsulate myoglobin, hemoglobin (Hb) (64 kDa), bovine serum albumin(BSA) (66 kDa), IgG (150 kDa), catalase (250 kDa), fibrinogen (340 kDa),and apoferritin (450 kDa).

The invention is intended to be illustrated but not limited by thefollowing examples.

EXPERIMENTAL

Comparative and quantitative studies were performed in order toestablish a generalizable method for producing scalable quantities ofneutrally-charge and fully PEGylated polymersomes that encapsulatefunctional protein. Differences in small molecule and proteinencapsulation were examined by employing polymersome formulationscomprised of OB18 and OB29 diblock copolymers. As described above withrespect to FIG. 2, these two PEO-b-PBD polymers and the polymersomesformed therefrom differ with respect to molecular weight and,ultimately, vesicle membrane thicknesses. Methylene blue (mBlue;Mw=319.85 g/mol) was used as a model small molecule and myoglobin (Mb;Mw=17,600 Da) as a model protein with unique biological function (i.e.,oxygen storage and release). FIG. 5A shows a representation ofpolymersomes made of amphiphilic diblock copolymers, as well aswater-insoluble agents and water-soluble species that may beencapsulated in or attached to polymersomes. For example, conventionalvesicle formation techniques that were employed to incorporatewater-soluble agents within PEO-b-PBD polymersomes included thin-filmrehydration and direct hydration, protocols for which are shown in FIGS.5B and 5C, respectively. The encapsulations of methylene blue andmyoglobin in PEO-b-PBD polymersomes generated by each of the thin-filmrehydration and direct hydration methods were compared. In order toquantify the encapsulation of fully functional protein capable of oxygenbinding, the iron concentration in polymersome-encapsulated myoglobinwas measured by ICP-OES, and the redox states of iron in the heme groupof myoglobin measured by UV-Vis absorption spectroscopy.

Compared to PEM created using existing techniques, PEM created byprogressive saturation exhibit an increase in the final concentrationsof Mb (e.g., from less than around 0.5 mg/mL in solution to greater thanaround 2.0 mg/mL in solution), and an increase in the final weight ratioof Mb to polymer that could be reproducible obtained (from less than 1w/w % Mb/polymer to greater than around 3-4 w/w % Mb/polymer). Further,PEM created by progressive saturation show an increase in the overallefficiency of protein encapsulation (from less than around 5% to greaterthan around 90%) in the PEM suspensions. Using cryo-TEM to verifyvesicle morphologies, suspensions of PEM developed using progressivesaturation display no signs of aggregate formation for longer than onemonth at 4° C., 23° C., and 37° C.

Materials

PEO(3900)-b-PBD(6500) (OB18) and PEO(1300)-b-PBD(2500) (OB29) werepurchased from Polymer Source (Dorval, Quebec, Canada). Horse skeletalmuscle Mb, bovine blood hemoglobin (Hb), bovine serum albumin (BSA),catalase (C), fibrinogen (F), sodium hydrosulfite, poly(ethylene glycol)dimethyl ether (PEG; Mn=˜500), protease from Streptomyces griseus(“pronase”), and dichloromethane (DCM) were purchased from Sigma-Aldrich(St. Louis, USA). Horse spleen apoferritin (aFr) was purchased from AlfaAesar (Ward Hill, USA) Immunoglobulin G (IgG) was purchased from LEEBiosolutions (St. Louis, USA). Dialysis tubing and vials were purchasedfrom Spectrum Laboratories (Rancho Dominguez, USA). Sodium chloride,potassium chloride, sodium phosphate dibasic, potassium phosphatemonobasic, mBlue, and Triton X-100 were purchased from Fisher Scientific(Suwanee, USA). All chemicals were of reagent grade unless otherwisestated.

The particle sizes were measured using Delsa™ Nano, a dynamic lightscattering (DLS) instrument (Beckman Coulter, Indianapolis, USA). Mb andmBlue concentrations were determined by absorption spectroscopy using aGenesys™ 10 S UV-Vis spectrophotometer (Thermo Scientific, Suwanee,USA). The concentrations of all proteins in polymersome suspension werefurther measured using a Micro BCA Protein Assay Kit, utilizing UV-Visspectrophotometry and by following the manufacturer's protocols (PierceBiotechnology, Inc; Rockford, Ill., USA). Iron concentrations inpolymersome-encapsulated Mb suspensions were determined using aVista-PRO CCD ICP-OES (Varian, USA). Oxygen equilibrium binding wasstudied using a Hemox™-Analyzer (TCS Scientific Corp, New Hope, Pa.,USA). Electro-formation was performed using Gene Pulser (Bio-Rad,Hercultes, Calif., USA).

Methods

Thin-Film Rehydration Method

10 mg of OB18 polymer was dissolved in 200 μL of DCM. The polymersolution was deposited on Teflon wafers (15 mm×15 mm) that weresubsequently dried for 30 min at room temperature (RT). The films werefurther kept under vacuum overnight at RT to ensure DCM evaporation. Formethylene blue encapsulation, polymer films were then hydrated withmethylene blue solution (21 mg/mL) in phosphate buffered saline (PBS; 10mM, pH 7.4) for 24-48 h at 23, 40 or 60° C. The samples were sonicatedfor 30 min at room temperature, followed by (×10) freeze-thaw cyclesusing liquid nitrogen. The samples were dialyzed (MW cutoff=100 kDa) for30 h at RT. For myoglobin encapsulation, polymer films were hydratedwith myoglobin solution (150 mg/mL) in PBS (10 mM, pH 7.4) for 60 h at23, 40, and 60° C. The samples were then sonicated for 30 min at RTfollowed by dialysis (MW cutoff=1000 kDa) for 30 h at 4° C.

Direct Hydration Method

10 mg of OB18 and 10 mg of PEG were heated in a 1.5 mL centrifuge tubefor 20 min at 95° C. The samples were mixed and cooled to roomtemperature, followed by the addition of 10 μL of methylene bluesolution (21 mg/mL) or myoglobin solution (150 mg/mL) in PBS (10 mM, pH7.4). The samples were then diluted with 20, 70, and 900 μL of PBS andwell mixed after each addition/dilution (via vortexing). The sampleswere then dialyzed for 30 h at room temperature or at 4° C. (molecularweight cutoff of 1000 kDa) to remove unencapsulated methylene blue ormyoglobin, respectively.

Quantification of mBlue/Mb

The amounts of methylene blue or myoglobin that were encapsulated inpurified polymersome suspensions were determined by measuring solutionabsorbance at 665 nm (mBlue) or at 410 nm (Mb), using a UV-Visspectrophotometer. Calibration curves for methylene blue and myoglobinwere developed using serial dilutions of known concentrations. Tomeasure the iron content in polymersome-encapsulated myoglobinsuspensions (as a corroboration of myoglobin concentration in thatsample), 5-10% (v/v) of Triton X-100 was added, the mixture was digestedby heating in aqua regia for 3 h at 98° C., and was subsequently dilutedwith deionized water. ICP-OES was performed on experimental samples andtheir iron content was determined in comparison to this standardcalibration curve. The concentrations of myoglobin (as calculated byUV-Vis absorbance spectroscopy) were compared to those obtained viaICP-OES or via the Micro BCA Assay (secondary UV-Vis method) for eachsuspension. Loading of aqueous encapsulants in the polymersomes wasquantified and expressed as the final weight percentages ofencapsulant-to-polymer that comprised the vesicles in suspension (e.g.,w/w % Mb/polymer).

Quantification of metMb

The amount of metmyoglobin (metMb, i.e., oxidized Mb with a Fe(III)-hemegroup) in polymersome suspensions was quantified using a modified UV-Visabsorption protocol that was previously established for the measurementof cyanomethemoglobin levels. In brief, the absorbance of myoglobin wasmeasured at 630 nm (L₁) against a blank reference (deionized water). Onedrop of KCN solution (1 part 10% KCN and 1 part 50 mM phosphate, pH 7.6)was added and mixed with the treated myoglobin samples. This reactionstep was necessary to convert metMb to cyanometmyoglobin (cyanoMb),which does not absorb at 630 nm. After 2 min, the absorbance wasmeasured at 630 nm (L₂) against the deionized water, which served as theblank reference. The concentration of metMb was determined usingEquation 1:

$\begin{matrix}{{{\lbrack {{met}\;{MB}} \rbrack\mspace{14mu}({mM})} = {\frac{L_{1} - L_{2}}{1 \times E} \times D_{1}}},} & ( {{Eq}.\mspace{11mu} 1} )\end{matrix}$where E=3.7 (cm×mM)⁻¹ and is the extinction coefficient of metMb at 630nm, and D₁ is the dilution factor in this experiment (cuvette length=1cm).

To determine the concentration of myoglobin, one drop of 20% K₃(Fe(CN)₆)was added and mixed with the treated myoglobin sample. The solution wasallowed to react for 2 min and an additional drop of 10% KCN was addedand mixed. The absorbance of the sample was then measured at 540 nm(L₃). The concentration of total Mb was determined using Equation 2:

$\begin{matrix}{{{\lbrack {{total}\mspace{14mu}{Mb}} \rbrack\mspace{14mu}({mM})} = {\frac{L_{3}}{1 \times E} \times D_{2}}},} & ( {{Eq}.\mspace{11mu} 2} )\end{matrix}$where E=11.3 (cm×mM)⁻¹ and is the extinction coefficient for cyanometMbat 540 nm; D₂ is the dilution factor (cuvette length=1 cm).

The percentage of metMb in the original solution was determined usingEquation 3:

$\begin{matrix}{{\lbrack {{met}\;{MB}} \rbrack(\%)} = {\frac{\lbrack {{met}\;{MB}} \rbrack}{\lbrack {{met}\;{MB}} \rbrack + \lbrack {{total}\mspace{14mu}{Mb}} \rbrack} \times 100.}} & ( {{Eq}.\mspace{11mu} 3} )\end{matrix}$

Structural Characterization of Polymersomes

Polymersome suspensions were diluted in PBS solution and theirhydrodynamic diameters were measured by DLS using a standard 1.5 mLsemi-micro Plastibrand polystyrene cuvette (VWR, Atlanta, USA). Themorphologies of blank polymersomes and polymersome-encapsulatedmyoglobin were visualized by cryo-TEM (JEOL 2100F, USA). In brief,polymersome samples were suspended in a microperforated grid, rapidlyvitrified using liquid ethane (−183° C.), and loaded onto a cryogenicsample holder for cryo-TEM imaging at 200 kV.

Encapsulation of mBlue and Mb in Polymersome Suspensions UsingConventional Methods

To establish a baseline for comparisons of small molecule and proteinencapsulation in polymersome suspensions, the final concentrations,weight percentages (i.e., weight of encapsulated agent compared to theweight of the polymer that comprises the nanoparticle), and efficienciesof encapsulation for methylene blue were determined with OB18polymersomes formed by the thin-film rehydration technique. FIG. 6Ashows the weight percentage results of the final polymersome compositionfor encapsulation of methylene blue at 40° C. (i.e., 4.1 w/w %mBlue/polymer) and 60° C. (i.e., 5.0 w/w % mBlue/polymer). Whenthin-film rehydration was attempted at room temperature (i.e., 23° C.),the encapsulation of methylene blue was found to be negligible (resultsnot shown), possibly due to the observation that the polymer films didnot swell after 48-72 h of hydration. PEO-b-PBD-based polymersomesrequire the input of energy for vesicle formation, which is usuallysupported by using elevated temperatures (e.g., greater than 45° C.).

To improve the efficiency of encapsulation at lower temperatures, whichwould be necessary when employing labile proteins, encapsulation ofmBlue was also studied by the direct hydration method. FIG. 6B shows thefinal weight percentage of mBlue-to-polymer in polymersome suspensionscreated using direct hydration at 23° C. (i.e., 1.2 w/w %mBlue/polymer).

Next, polymersome-encapsulated myoglobin suspensions formed at 23° C. bythin-film rehydration were initially found to be comprised of around 2.7w/w % Mb/polymer. After the addition of a proteolysis step to any removesurface-associated Mb (i.e., free protein that was nonspecificallybound), the final composition of the polymersomes was found to be only0.5 w/w % Mb/polymer, indicating that very small amounts of protein werebeing encapsulated within polymersomes. FIG. 6C shows the final weightpercentage of Mb-to-polymer in polymersome suspensions created usingthin-film rehydration at 23° C. both before and after the addedproteolysis step.

In order to improve the concentrations and the final weight percentagesof myoglobin in polymersome-encapsulated myoglobin suspensions,polymersome generation at higher temperatures was again attemptedutilizing thin-film rehydration at 40 and 60° C. Such tests, however,only resulted in protein denaturation and aggregation. In contrast,polymersome-encapsulated myoglobin suspensions prepared by directhydration at 23° C. displayed good colloidal properties and thecharacteristic absorption spectra of intact myoglobin, yet the finalloading ratio of Mb-to-polymer in these polymersome-encapsulatedmyoglobin suspensions was low. FIG. 6D shows the final weight percentageof Mb-to-polymer in polymersome suspensions created using directhydration at 23° C. both before proteolysis (i.e., showing 0.3 w/w %Mb/polymer) and after proteolysis (i.e., 0.1 w/w % Mb/polymer).

Modifications to Conventional Processes

Features of both the direct hydration and thin-film rehydrationtechniques were iteratively evaluated in experimental conditions inorder to improve polymersome-encapsulation of functional protein.

Effects of Sonication

Following the direct hydration protocol, upon addition of OB18 polymerand PEG, the sample was mixed, cooled to RT, and 10 μL of Mb solution(150 mg/mL) in PBS (10 mM, pH 7.4) was added. The sample was thenfurther diluted with 10, 20, 50, and 100 μL of Mb solution, followed bymixing and sonication for either: A) 0 min or B) 30 min after eachadditional dilution step. All samples were then dialyzed for 30 h at 4°C. (molecular weight cutoff of 1000 kDa). The final Mb concentrations,weight percentages of Mb-to-polymer, and the efficiencies for Mbencapsulation in the resultant polymersome suspensions were measured byUV-Vis absorption spectroscopy, ICP-OES and compared.

In attempting encapsulation of Mb in OB18 polymersomes, and by employingthe direct hydration protocol for vesicle formation, the weight ratiosof Mb-to-polymer that were reproducibly obtained in the final PEMsuspensions were found to again be very low (e.g., around 0.2 w/w %Mb/polymer). The encapsulation efficiency, however, could be increasedby more than 30 times if the samples were sonicated for 30 min at roomtemperature after each dilution step (i.e., sonicating after introducingadditional volumes of aqueous solution to dilute the concentration ofpolymer in suspension). As discussed above with respect to FIG. 3A, therelative amount of Mb in PEM suspension could be increased to around 6.0w/w % Mb/polymer, supporting the addition of this sonication step to theoriginal direct hydration protocol.

Effects of Blending Technique (Dissolving Polymer in Organic Solvent Vs.Addition of Heat)

The effects of utilizing an organic solvent were compared to adding heatto blend OB18 with a PEG500 homopolymer to improve polymer dissolutionduring the first step of the direct hydration protocol. These strategieswere compared with respect to the final yield of polymersome formationand, ultimately, to the concentrations and efficiencies of proteinencapsulation that could be obtained by each method. If the two polymerswere first mixed by dissolution in DCM (followed by polymersomeformation after organic solvent evaporation), the final weight ratio ofMb-to-polymer in PEM suspensions was around 2 w/w % Mb/polymer. Incomparison, initial heating of dry OB18 and PEG500 to 95° C. for 1 himproved mixing and promoted more efficient polymersome generation,yielding a significantly higher final weight ratio of Mb-to-polymer inthe final PEM suspensions (i.e., around 5 w/w % Mb/polymer),corresponding to a greater amount of encapsulated protein.

Following the direct hydration protocol, 10 mg of OB18 and 10 mg of PEGwere either blended by heating at 95° C. for 1 h, or mixed bydissolution in DCM (50 μL) followed by drying under vacuum at roomtemperature overnight. Further encapsulation was done using the sameprotocol with the addition of 30 min of sonication after each dilutionstep. Mb concentrations in the final suspensions were determined byUV-Vis absorption spectroscopy and ICP-OES and compared.

Effects of Mb Oxidation State (i.e., Utilizing oxyMb vs. metMb forPolymersome-Encapsulation)

Myoglobin encapsulation was found to be further augmented when thestarting Mb stock solution was first reduced with sodium dithionite toconvert all metmyoglobin (i.e., metMb) to the oxmyoglobin (i.e., oxyMb)form. OxyMb contains a central heme group with iron in the ferrous state(i.e., Fe(II)), which improves the solubility of the protein whencompared it its metMb form that contains Fe(III). This oxyMb solutionwas further desalted via dialysis prior to its utilization in all of thesubsequent dilution steps in the direct hydration protocol, which wasfound to be necessary to increase the loading of Mb in PEM suspensions(i.e., the final weight ratio of Mb-to-polymer). As discussed above withrespect to FIG. 3B, when oxyMb was used in the initial protocol step,PEM suspensions comprised of 6 w/w % Mb/polymer were formed, which was astatistically significant improvement over the 4 w/w % Mb/polymerobtained when metMb was utilized.

The direct hydration protocol was modified to expose the initial mixtureof polymer and PEG to 1 h (instead of 20 min) of heating at 95° C. Theeffect of the iron oxidation state of the heme group of Mb on theefficiency of polymersome-encapsulation was studied by using oxyMb(i.e., Fe(II)Mb) vs. metMb for each dilution step. MetMb solution wasprepared by dissolving lyophilized Mb in PBS; the same solution wastreated with 1 wt % Na₂S₂O₄ to obtain the reduced Mb form (oxyMb). Mbencapsulation in polymersomes was measured by UV-Vis absorptionspectroscopy and ICP-OES, and compared.

Effects of Sonication and Temperature on Mb Oxidation

More than 40% of the oxyMb that was used in the initial step forpolymersome-encapsulation was found to be reoxidized to metMb within 2 hat 50° C. In contrast, only around 15% metMb was generated from theinitial oxyMb solution if lower temperatures were employed forpolymersome formation (e.g., heating for 2 h at 40° C.). The rate of Mboxidation at 50° C. was also significantly higher than that at 40° C.,regardless of the addition of sonication or the power that was utilized,as discussed above with respect to FIG. 3C. As such, it was determinedthat sonication had no effect on Mb oxidation and it was thuspreferentially employed to both promote polymer mixing and to provideinterfacial energy to augment polymersome formation.

The initial Mb solution (at 150 mg/mL) was reduced with Na₂S₂O₄ andsubjected to various conditions, including heating at 40° C. (with orwithout sonication) or at 50° C. for 2-5 h. Mb oxidation was determinedby measuring the percentages of metMb in the totalpolymersome-encapsulated Mb suspensions, using the cyanomethemoglobinmethod.

Effects of Proteolysis

Upon formation, PEM suspensions were treated with 0.4% pronase solutionfor up to 18 h at room temperature in order to examine the duration oftime required for the complete digestion of any surface-associated(i.e., non-specifically bound) Mb. It was observed that allsurface-associated Mb was digested in 2 h and that neither increasingpronase exposure time nor concentration further augmented Mb loss, thusindicating that only encapsulated Mb was retained, as discussed abovewith respect to FIG. 3D.

Mb was encapsulated in OB18 polymersomes using different initialsolution concentrations of protein (i.e., 50, 75, and 150 mg/mL)followed by dialysis for at least 30 h at 4° C. (molecular weight cutoffof 1000 kDa). The samples were subsequently treated with 0.4 wt %pronase solution for 18 h at room temperature and again dialyzedovernight at 4° C. Mb encapsulation in polymersomes (before and afterproteolysis) was measured by UV-Vis absorption spectroscopy and ICP-OES,and compared.

Improvement of Mb encapsulation efficiency (i.e., % Mb EE)

Five sets of experiments were done with various Mb-to-PBS volume ratios(i.e., “Mb:PBS”) in order to establish the optimal Mb concentration touse in each subsequent dilution step in our modification of the original“direct hydration” protocol. Notably, when the Mb:PBS increased, thefinal w/w % Mb/polymer in the PEM suspensions also increased; but, theMb encapsulation efficiency (i.e., % Mb EE) decreased as a result. Inother words, the final Mb-to-polymer mass ratio was maximized when alldilutions steps were conducted using a maximally concentrated Mbsolution (i.e., Mb:PBS=190:0 and 150 mg/mL oxyMb). As discussed abovewith respect to FIG. 3E, the % Mb EE was largest when the Mb:PBS wasminimal (i.e., 10:180). As the amount of protein in the finalpolymersome suspension is ultimately the metric that must be optimizedfor therapeutic administration (in order to minimize the amount ofassociated carrier polymer that is introduced to a subject), it wasdetermined that a pure Mb solution (150 mg oxyMb/mL) would be used foreach dilution step in the ultimate encapsulation protocol, maximizingthe final w/w % Mb/polymer in PEM suspensions.

Following the basic direct hydration protocol, 10 mg polymer and 10 mgof PEG were initially heated in 1.5 mL microcentrifuge tubes for 1 h at95° C. and subsequently cooled to RT. The mixtures were then diluted byadding 10, 10, 20, 50, and 100 μL of diluents. Two different solutionswere used and compared for each of the 5 dilution steps: PBS and/or Mbsuspensions (i.e., 150 mg/mL Mb in PBS). The final (v/v) ratio of Mb toPBS (i.e., “Mb:PBS”) used as diluents in steps 1, 2, 3, 4, and 5 were10:180, 20:170, 40:150, 90:100, and 190:0, respectively. The sampleswere then proteolyzed using 0.4 wt % pronase and again dialyzedovernight at 4° C. (molecular weight cutoff of 1000 kDa). Mbencapsulation was measured using UV-Vis absorption spectroscopy. The Mbencapsulation efficiencies were calculated using Equation 4:

$\begin{matrix}{{{{Mb}\mspace{14mu}{Encapsulation}\mspace{14mu}{Efficiency}} = {\lbrack {1 - \frac{{v_{1}c_{1}} - {v_{2}c_{2}}}{v_{1}c_{1}}} \rbrack \times 100}},} & ( {{Eq}.\mspace{11mu} 4} )\end{matrix}$Where v₁=Initial volume of the unencapsulated Mb (mL), c₁=Initialconcentration of unencapsulated Mb (mg/mL), v₂=volume ofpolymersome-encapsulated Mb obtained after dialysis and proteolysis(mL), and c₂=concentration of encapsulated Mb obtained after dialysisand proteolysis (mg/mL)

Using Progressive Saturation to Generate Polymersome-EncapsulatedProtein Suspensions.

By incorporating each of the steps in the various embodiments, aprogressive saturation technique was established, represented in FIG.7A, which vastly improved upon the results of the original directhydration protocol discussed above with respect to FIG. 5C. Using theprogressive saturation protocol, the final content of Mb in OB18-basedPEM suspensions was found to be 6.1 and 3.2 w/w % Mb/polymer before andafter proteolysis, respectively. Quantification of the iron content(numbers of intact heme groups) in each of the polymersome suspensionsby ICP-OES corroborated UV-Vis measurements of protein concentration. Asshown in FIG. 7B, the final loading ratios of Mb in the polymersomeswere found to be 7.9 and 5.1 w/w % Mb/polymer before and afterproteolysis, respectively. As shown in FIG. 7C, the percentage of metMb(with respect to the total Mb content in these suspensions) wasdetermined by UV-Vis absorbance spectroscopy and found to be around 8%and 6% in non-proteolyzed (PEM-SE) and proteolyzed (PEM-E) samples,respectively. FIG. 7D is a table of the measured properties (i.e.,results) for the OB18-based PEM suspensions, as discussed with respectto FIGS. 7B and 7C.

Stability of Polymersome-Encapsulated Protein Suspensions

OB18-encapsulated Mb suspensions were prepared using the optimizedprogressive saturation technique. The samples were stored at 4, 23, and37° C. for 3 weeks. At predetermined time points, the samples werediluted with PBS and the mean particle size and distributions weredetermined by DLS.

Equilibrium Binding of Oxygen in Polymersome-Encapsulated Mb Suspensions

The equilibrium binding and dissociation curves for oxygen insuspensions of free and polymersome-encapsulated Mb were obtained at 37°C. using a Hemox™-Analyzer. Samples were allowed to saturate to a pO₂ of147 mmHg (using compressed air) and then deoxygenated (using acompressed nitrogen stream). The absorbance of oxygenated anddeoxygenated free and polymersome-encapsulated Mb suspensions wasrecorded as a function of pO₂ via dual wavelength spectroscopy. Oxygenequilibrium curves were fit to a four-parameter (A₀, A_(∞), P₅₀, n) Hillmodel (Equation 5). In this model, A₀ and A_(∞) represent the absorbanceat 0 mmHg and at 147 mmHg, respectively. The pO₂ represents the partialpressure of oxygen; and, P₅₀ represents the partial pressure of O₂ wherethe sample is 50% saturated with oxygen. Lastly, n represents thecooperativity coefficient for the sample.

$\begin{matrix}{Y = {\frac{{Abs} - A_{0}}{A_{\infty} - A_{0}} = {\frac{p\; O_{2}^{n}}{{p\; O_{2}^{n}} + P_{50}^{n}}.}}} & ( {{Eq}.\mspace{11mu} 5} )\end{matrix}$

FIG. 7E shows the P₅₀ values (in mmHg) obtained for a free myoglobin(Mb) sample, a polymersome-encapsulated myoglobin sample prior toproteolysis (PEM-SE) that was prepared using the progressive saturationtechnique, and a polymersome-encapsulated myoglobin sample after pronasetreatment (PEM-E) that was prepared using the progressive saturationtechnique.

Characterization of the Final PEM Suspensions

The size distributions of the final OB18- and OB29-based PEM suspensionswere measured by both DLS and cryo-TEM. FIG. 8A provides the averagehydrodynamic diameter of particles in OB18-based and OB29-based PEMsuspensions prepared using progressive saturation, as assessed by DLS.Cryo-TEM images of vesicles in OB18-based and OB29-based PEM suspensionsare shown in FIGS. 8B and 8C, respectively. These results confirmed amean particle diameter of approximately 200 nm for OB18 polymersomes,and 130 nm for OB29 polymersomes. The stability of the OB18-based PEMsuspensions were further examined over three weeks and at varioustemperatures, with the polymersomes, demonstrating no aggregation basedon the consistent particle numbers and stable size distributions insuspension. FIG. 8D shows the average hydrodynamic diameters ofparticles, as determined by DLS, in OB18-based PEM suspensions that wereprepared by progressive saturation at various temperatures (i.e., 4° C.,23° C., and 37° C.) as a function of time. Finally, the functionalstatus of encapsulated Mb in the PEM suspensions (i.e., retention ofMb's ability to bind and release oxygen) was verified by dual wavelengthspectroscopy. FIG. 8E shows oxygen equilibrium curves for free oxyMb andoxygenated OB18-based PEM suspensions. Error bars denote standarddeviation of the mean. n≥3 experimental replicates per condition. Theoxygen equilibrium curves, P₅₀ (i.e., the partial pressure of O₂ wherethe Mb is 50% saturated with oxygen) of PEM were very similar to thoseof free Mb in solution.

Polymersome-Encapsulation Using Block Copolymers and Proteins of VaryingMolecular Weight

The generalizability of the progressive saturation technique was testedusing proteins of various sizes: i.e., Mb (17 kDa), hemoglobin (Hb; 64kDa), bovine serum albumin (BSA; 66 kDa), immunoglobulin G (IgG: 150kDa), catalase (250 kDa), fibrinogen (340 kDa), and apoferritin (450kDa); each protein was dissolved in PBS (10 mM, pH 7.4) at its maximalsolubility, corresponding to final suspension concentrations of 150,150, 40, 20, 50, 50, and 25 mg/mL, respectively. The progressivesaturation protocol was followed to encapsulate these proteins in OB29polymersomes. Free proteins were separated by dialysis for at least 30 hat 4° C. (molecular weight cutoff of 1000 kDa). Surface associatedprotein was removed by proteolysis via treatment with 0.4 wt % pronasesolution followed by overnight dialysis at 4° C. (molecular weightcutoff of 1000 kDa). Protein encapsulation (before and afterproteolysis) in polymersome suspensions was quantified via the micro-BCAassay, utilizing UV-Vis spectrophotometry and by following themanufacturer's protocols (Pierce Biotechnology, Inc; Rockford, Ill.,USA). The final concentrations of protein were divided by those ofpolymer and expressed as the final weight ratios of protein-to-polymerthat comprised the polymersomes in suspension (e.g., w/w % Mb/polymer).

Statistical Analysis

Data are presented as the mean±the standard deviation of the mean (SD).A minimum of three experimental replicates was used for each condition.One-way analysis of variance (ANOVA) was conducted using GraphPadsoftware (San Diego, USA). A p value of <0.05 was consideredstatistically significant.

What is claimed is:
 1. A composition, comprising: a suspension of apolymersome-encapsulated functional protein, wherein the suspension isprepared by: thermally blending a quantity of an amphiphilic diblockcopolymer with a quantity of polyethylene glycol (PEG), wherein theamphiphilic diblock copolymer comprises poly(ethyleneoxide)-block-poly(butadiene) (PEO-b-PBD); adding an aliquot of asolution of the functional protein to a sample containing thePEG/polymer formulation, wherein the solution of the functional proteincomprises oxymyoglobin or metmyoglobin in phosphate buffered saline(PBS); and performing at least one dilution step such that polymersomesthat are generated are progressively saturated with the functionalprotein.
 2. The composition of claim 1, wherein preparing the suspensionof a polymersome-encapsulated functional protein comprises: thermallyblending a quantity of an amphiphilic diblock copolymer with a quantityof polyethylene glycol (PEG) for at least 30 minutes, wherein thethermal blending is performed at 90-100° C.; mixing and cooling aresulting PEG/polymer formulation to room temperature; adding an aliquotof a solution of the functional protein to a sample containing thePEG/polymer formulation, wherein a ratio of the added aliquot to thePEG/polymer formulation is between around 0.5:1 and around 1.5:1 byvolume; and performing at least three dilution steps such thatpolymersomes that are generated are progressively saturated with thefunctional protein, wherein each dilution step comprises: adding to thesample an additional amount of the solution of the functional protein;mixing a resulting dispersion of the functional protein in thePEG/polymer formulation; and sonicating the resulting dispersion for atleast 30 minutes.
 3. The composition of claim 2, wherein performing theat least three dilution steps comprises performing a first, a second,and a third dilution step in a serial fashion, wherein: adding theadditional amount of the solution in the first step comprises adding afirst amount of the solution of the functional protein such that a ratioof the first amount to the PEG/polymer formulation is around 1:1 byvolume; adding the additional amount of the solution in the second stepcomprises adding a second amount of the solution of the functionalprotein such that a ratio of the second amount to the PEG/polymerformulation is around 2:1 by volume; and adding the additional amount ofthe solution in the third step comprises adding a third amount of thesolution of the functional protein such that a ratio of the third amountto the PEG/polymer formulation is around 5:1 by volume.
 4. Thecomposition of claim 3, wherein performing the at least three dilutionsteps further comprises performing a fourth dilution step, whereinadding the additional amount of the solution in the fourth stepcomprises adding a fourth amount of the solution of the functionalprotein such that a ratio of the fourth amount to the PEG/polymerformulation is around 5:1 by volume.
 5. The composition of claim 4,further comprising removing surface-associated protein from polymersomesin the suspension of the polymersome-encapsulated functional protein,after the at least three dilution steps using proteolysis.
 6. Thecomposition of claim 5, wherein using proteolysis comprises: treatingthe PEG/polymer/protein sample with a 0.4 wt % pronase solution for atleast 18 hours at room temperature; and allowing dialysis of the mixedPEG/polymer/protein sample at 4° C. for at least twelve hours.
 7. Thecomposition of claim 1, wherein the solution of the functional proteincomprises a 150 mg/mL solution of oxymyoglobin in phosphate bufferedsaline (PBS).
 8. The composition of claim 7, further comprisingpreparing the solution of the functional protein by: combining asolution of 150 mg/mL metmyoglobin (metMb) in phosphate buffered salinewith sufficient amount of 1 wt % sodium dithionite (Na₂S₂O₄) to reduceto the metMb to oxymyoglobin (oxyMb).
 9. The composition of claim 1,wherein thermally blending the quantity of the block copolymer with thequantity of the low molecular weight PEG for at least 30 minutescomprises thermally blending 5-15 mg of poly(ethyleneoxide)-block-poly(butadiene) (PEO-b-PBD) with 5-15 mg of 500 kDa PEG(PEG500) for at least one hour.
 10. The composition of claim 1, wherein:thermally blending the amphiphilic diblock copolymer with the lowmolecular weight PEG for at least 30 minutes comprises thermallyblending 10 mg of poly(ethylene oxide)-block-poly(butadiene) (PEO-b-PBD)with 10 mg of 500 kDa PEG (PEG500) for one hour; and adding the aliquotof the solution of the functional protein comprises adding 10 μL of anoxymyoglobin solution to the sample of the PEG/polymer formulation. 11.The composition of claim 1, wherein the thermal blending is performed ataround 95° C.